The welding strength of polyvinyl chloride film shall be measured in the welding performance test. The test shall be carried out on test equipment that can be adjusted and controlled at will. The highest temperature at the weld can be measured with an automatic thermometer. The general situation of welding temperature is as follows:
hard polyvinyl chloride film 150 ~ 170 ℃
soft PVC film 120 ~ 170 ℃
heat sealing film 90 ~ 120 ℃
pull the welded plastic film sample hard by hand, the weld itself should not crack, and the crack must be next to the weld. This is a sign to judge the quality of welds.
cut the weld vertically, and the obtained cross section and Figure 3-Cross-sectional drawings in 49 are compared. Figure 3- The section of 49e is the normal section of high frequency Weld, thus reasonable welding conditions can be determined.
The thickness of the weld seam can only be at most 1/2 of the total thickness of the original two films. The circular flange weld marks on both sides of the weld shall be uniform, symmetrical and free of bubbles.
The symmetry and uniformity of high-frequency welds are closely related to whether the weld strength presents a maximum value.
As outdoor enthusiasts, we understand the importance of keeping our gear safe from the elements.
Planning a camping or hiking trip can be an exciting endeavor, but it's important to be prepared for whatever weather conditions might come your way.
PVC tarpaulin is a versatile and durable material that is commonly used for a wide range of applications.
Tarpaulins are a staple in many industries, often serving as reliable covers for machinery, equipment, and other items that need protection from the elements.
Contacts: Charlie Chan
Tel: +86-760-23759163
Fax: +86-760-23759197
E-mail: ly27@tsaiyang.com / ly07@tsaiyang.com
WhatsApp/Wechat: 0086-13590950659
ADD: No.22 Yixian Road, Huoju Development Zone, Zhongshan, Guangdong, China.